great Job Dan! the channel is one of my favorites! MP

I like the HHS or Cobalt bits for steel and the vanadium for stainless. I get all of my dill bits from McMaster Carr or MSC cheap box store bits don't...

we use a O2 cylinder with the top cut off, works well. we had been using a 4"/4" square tube before we switched to a faster oil. that also worked well...

very good work. I love the head knife as well, was that for you or some one else? MP

I will third what carl said, I also switched to stencils for the most part about a year ago. I also got mine from Patrica, nothing but good things to ...

OK I'll start. My business partners and I started stabilizing last winter, after a few weeks we came up with a set of best practices to get good c...

with that much time at temp in a oven I would think the decarb may be fooling you into thinking it may have not hardened, try grinding 10-15 thou off ...

I had a 14" hendly for years, never used it, i passed it along and now have two southbend 9" I have not found them to limit what i can do other than ...

I have a tank of corrupted ferric (bronze dust) that I use to descale L6 (nastiest scale of any steel i have ever worked with) takes 2-4 hours and no ...

I have used paste wax after force drying that works well, alternately I have used a heat gun to warm the leather and drive off some moisture then brus...

I've been using cactus juice for stabilizing for the last year, I have not had any of the problems Ed mentioned. Nor has anyone else I have spoken wit...

Away from home and posting from my phone so this will be short. I have developed a reaction to just about all of the rosewoods and most importantly...