thanks for the great questions guys, I'll leave this open until tomorrow night if any one has any other questions. MP

great Job Dan! the channel is one of my favorites! MP

I like the HHS or Cobalt bits for steel and the vanadium for stainless. I get all of my dill bits from McMaster Carr or MSC cheap box store bits don't...

we use a O2 cylinder with the top cut off, works well. we had been using a 4"/4" square tube before we switched to a faster oil. that also worked well...

very good work. I love the head knife as well, was that for you or some one else? MP

I will third what carl said, I also switched to stencils for the most part about a year ago. I also got mine from Patrica, nothing but good things to ...

OK I'll start. My business partners and I started stabilizing last winter, after a few weeks we came up with a set of best practices to get good c...

with that much time at temp in a oven I would think the decarb may be fooling you into thinking it may have not hardened, try grinding 10-15 thou off ...

I had a 14" hendly for years, never used it, i passed it along and now have two southbend 9" I have not found them to limit what i can do other than ...

I have a tank of corrupted ferric (bronze dust) that I use to descale L6 (nastiest scale of any steel i have ever worked with) takes 2-4 hours and no ...

I have used paste wax after force drying that works well, alternately I have used a heat gun to warm the leather and drive off some moisture then brus...