Hello Boris and welcome. When you have questions ask away. We will do our best to answer them. Good to have you in the ABS and on the forum. Brion
Hello Hunter. With W2 the go to quenchant is Parks 50. Yes you can use water, but you risk cracking the blade and it happens fairly often with water. ...
Excellent choice Hunter. What will you be using for the quenchant? Brion
I use satanite Hunter and get good results. Rutlands furnace cement works also. If you use rutlands, be sure to let it dry thoroughly before heating f...
Hey Hunter. The traditional wood for a Japanese sword scabbard and handle is a species of magnolia found in Japan. Called Ho wood. We can get it over ...
Excellent answers everyone! The main thing is do it for you. Have MS and JS look at your knives and give feedback as to what you need to improve on. I...
I would just get the diamond burr set to start Don. They work fine and the set has different diameters. I get my sets from RioGrande jewelry supply. A...
Hello Don. I would recommend the SR series, which is reversible. Comes in handy. For general work the H30 handpiece is great. With the right burrs it ...
Looking good Adam, and W2 and parks50 is what I would have recommended. What temp did you quench at? The quench temp plays a big role in activity, as ...
Hello Adam. To answer your question, yes, symmetry will help. There was one school of Japanese smiths who had different hamon designs on each side of ...
Hey Kale I wish I could but I do not do private classes at my shop. Liability and insurance reasons. I do teach at Texarkana College where the Bill Mo...
I just tried and am getting the same thing Kale. I will let the administrator know. Brion